Carpet Waste Composite and Method for Making Same

ABSTRACT

A carpet waste composite and method for making the same are disclosed. In one embodiment of the method, unadulterated layers of carpet having a backing side and a tufted side are provided. An initial unfused carpet layer is made by placing two cleaned, unadulterated layers of carpet tufted side-to-tufted side with homogenous and non-adhesive, non-binding contact therebetween. Heat and pressure followed by cooling are applied to furnish an initial fused carpet layer. An iterative unfused carpet layer is created by placing two cleaned, unadulterated layers of carpet tufted side-to-tufted side with the initial fused carpet layer interposed therebetween using non-adhesive, non-binding contact. Heat and pressure followed by cooling are applied to furnish an iterative fused carpet layer. The process of adding layers may continue as required.

PRIORITY STATEMENT & CROSS-REFERENCE TO RELATED APPLICATION

This application claims priority from co-pending U.S. Patent Application No. 62/715,401 entitled “Carpet Waste Composite and Method for Making Same” filed on Aug. 7, 2018, in the name of Daniel R. McIntyre; which is hereby incorporated by reference for all purposes.

TECHNICAL FIELD OF THE INVENTION

This invention relates, in general, to composites and, in particular to carpet waste composites and a method for making the same that are used in various industrial, construction, and consumer applications requiring tensile strength and resistance to environmental factors including ultraviolet light and insects, for example.

BACKGROUND OF THE INVENTION

With increased emphasis on recycling and re-use, attention has turned to alternatives to disposing of carpet waste in landfills, whether the carpet waste is a result of new carpet production or post-consumer use. As composites may be used in various industrial, construction, and consumer applications requiring tensile strength and resistance to environmental factors including ultraviolet light and insects, for example, efforts are focused on diverting carpet waste from landfills and utilizing the carpet waste in the production of composites. In fact, some studies indicate as much as 6 billion pounds of carpet waste may be deposited in landfills in the United States each year. A need exists for carpet waste composites with acceptable performance that may be efficiently and effectively manufactured.

SUMMARY OF THE INVENTION

It would be advantageous to achieve a carpet waste-based composite that performs in various industrial, construction, and consumer applications. It would also be desirable to enable a thermomechanical solution that furnishes an effective and efficient process for the production of composites with carpet waste sourced from landfill diversion and new carpet production. To better address one or more of these concerns, in one aspect of the invention, a carpet waste composite and method for making the same are disclosed. In one embodiment of the method, unadulterated layers of carpet having a backing side and a tufted side are provided. An initial unfused carpet layer is made by placing multiple cleaned, unadulterated layers of carpet tufted side-to-tufted side with homogenous and non-adhesive, non-binding contact therebetween. Heat and pressure followed by cooling are applied to furnish an initial fused carpet layer. An iterative unfused carpet layer is created by placing multiple cleaned, unadulterated layers of carpet tufted side-to-tufted side with the initial fused carpet layer interposed therebetween using non-adhesive, non-binding contact. Heat and pressure followed by cooling are applied to furnish an iterative fused carpet layer. The process of adding layers may continue as required.

In other aspects of the teachings presented herein, variations in the methodology are disclosed and taught. By way of example, the layers of carpet may be positioned tufted side-to-backing side or backing side-to-backing side at various stages in the methodology. Different numbers of multiple layers of carpet, such as two or four or more, may be used initially or at other stages of the methodology to create the unfused carpet layer. In another aspect, the unadulterated layers of carpet may include by weight percent, 1% to 5%, for example, of additives. By way of a further aspect, the layers of carpet may include adhesive and binding contact therebetween provided by an adhesive or other binder of by weight percent, 1% to 5%, for example. These and other aspects of the invention will be apparent from and elucidated with reference to the embodiments described hereinafter.

BRIEF DESCRIPTION OF THE DRAWINGS

For a more complete understanding of the features and advantages of the present invention, reference is now made to the detailed description of the invention along with the accompanying figures in which corresponding numerals in the different figures refer to corresponding parts and in which:

FIG. 1 is a schematic depicting one embodiment of a carpet waste composite manufactured from carpet waste, according to the teachings presented herein; and

FIG. 2 is a schematic flow chart depicting one embodiment of a method for making a carpet waste composite according to the teachings presented herein.

DETAILED DESCRIPTION OF THE INVENTION

While the making and using of various embodiments of the present invention are discussed in detail below, it should be appreciated that the present invention provides many applicable inventive concepts which can be embodied in a wide variety of specific contexts. The specific embodiments discussed herein are merely illustrative of specific ways to make and use the invention, and do not delimit the scope of the present invention.

Referring initially to FIG. 1, therein is depicted one embodiment of a carpet waste composite, which is schematically illustrated and generally designated 10. The carpet waste composite 10 is shown as a rectangular support member 12 having a body 14 with sides 16, 18, 20, 22 and ends 24, 26. Although the carpet waste composite 10 is depicted as a rectangular support member 12, it should be appreciated that the carpet waste composite may take any form for various industrial, construction, and consumer applications. The carpet waste composite 10 may be used as a rail tie, a crossing tie, or in another rail application. Additionally, the carpet waste composite 10 may be utilized in various construction applications needing deck supports, bridge supports, beams, and other support members. Further, it should be appreciated that although the carpet waste composite 10 is depicted as having a rectangular shape, the shape may vary and be engineered, shaped, and angled according to the needs of the particular application.

The carpet waste composite is manufactured from carpet waste 30, which may be sourced from landfill diversion or new carpet production, for example. In one embodiment, the carpet waste 30 includes a backing side 32 having a tuft side 34 extending therefrom. The backing side 32 may include a primary backing fabric 36 and a secondary backing fabric 38 with a binding agent 40 bonding the primary backing fabric 36 to the secondary backing fabric 38. As depicted, the primary backing fabric 36 of the backing side 32 is located in contact with the tuft side 34. The backing side 32 provides tuft binds for securing the tuft side 34 to the carpet, imperviousness to moisture and resistance to edge raveling. The tuft side 34 includes face yarns 42 and offers carpet characteristics such as durability, abrasion resistance, texture retention, stain and soil resistance, colorfastness, ease of cleaning, and color clarity, for example.

The waste carpet may be sourced from various carpets, such as polypropylene carpets, nylon 6 carpets, nylon 6,6 carpets, and polyester carpets, or combinations thereof, for example. The vast majority of carpets manufactured in the United States are tufted carpets and that of all tufted carpets, the vast majority are manufactured with thermoplastic face yarns. Major face yarn types currently used in the manufacture of tufted carpets are nylon yarns, normally composed of poly(epsilon-caprolactam) or poly(hexamethylene adipamide), also known as nylon-6 and nylon 6,6, respectively; propylene polymer yarns, typically composed of propylene homopolymer; and polyester yarns, normally composed of polyethylene terephthalate. Primary backings for tufted carpets are typically woven fabrics made of synthetic yarns, although nonwoven fabrics can also be used. The most common synthetic material used in primary backings is polypropylene, although polyesters also find use in the industry. Again, it will be appreciated that the vast majority of backings for tufted carpets are manufactured from thermoplastics. The carpet finishing operation typically involves application of a latex binder (typically a filled thermoset resin emulsion) and a secondary backing. The material most typically used for carpet back coating is styrene butadiene latex (SBR), usually a carboxylated SBR. The overwhelming majority of tufted carpet today is finished by laminating a secondary backing to the tufted primary with a latex.

Referring to FIG. 2, therein is depicted one embodiment of a method for making the carpet waste composite 10. At block 50, a supply of cleaned, unadulterated layers of carpet 52, 54 are provided, which in one embodiment includes the aforementioned waste carpet 10. Although cleaned, unadulterated layers of carpet 52, 54 are provided, it should be appreciated that the supply of carpet may be uncleaned and adulterated. The supply of cleaned, unadulterated layers of carpet 52, 54 may be the same type of carpet or different types of carpet. That is, the systems and methods presented herein may be utilized with mixed carpet stock. The cleaned, unadulterated layer of carpet 52 includes a backing side 56 and a tuft side 58. In one implementation, the backing side 56 is not separated from the tuft side 58. That is, the carpet 52 may be unseparated. Further, the cleaned, unadulterated layer of carpet 52 may be unshredded and without grinding as unground. In one embodiment, intact carpet that is unseparated, unshredded, and unground is utilized. The cleaned, unadulterated layer of carpet 54 includes a backing side 60 and a tuft side 62. In one implementation the backing side 60 is not separated from the tuft side 62. That is, the carpet 54 may be unseparated. Further, the cleaned, unadulterated layer of carpet 54 may be unshredded and without grinding as unground. As previously mentioned, the cleaned, unadulterated layers of carpet 52, 54 may be sourced from various carpets, such as aforementioned polypropylene carpets, nylon 6 carpets, nylon 6,6 carpets, and polyester carpets, or combinations thereof, for example. The cleaned, unadulterated layers of carpet 52, 54 may be carpet waste that is sourced from landfill diversion or scraps and remainder pieces from new carpet production. The cleaned, unadulterated layers of carpet 52, 54 may be cleaned by a thorough combing and vacuuming to remove any debris. In one embodiment, during the cleaning process, additional compounds and chemicals are not added, so that the carpet 52, 54 is unadulterated.

At block 64, an initial unfused carpet layer 66 is created by placing cleaned, unadulterated layers of carpet 52, 54 tufted side-to-tufted side with homogenous and non-adhesive, non-binding contact therebetween. As shown, in one implementation, no adhesive and no binder are placed between the cleaned, unadulterated layers of carpet 52, 54.

At block 68, heat H and pressure P are applied to the unfused carpet layer 66 within a carrier 70 having vertically spaced plates 72, 74 at a fixed height F₁. By way of example and not by way of limitation, the vertically spaced plates 72, 74 may comprise aluminum plates. Further, the heat H and pressure P operations may be executed by a heated conveyor.

In one embodiment, the fixed height F₁ may be a distance from 80 thousandths of an inch (0.20 cm) to 280 thousand of inches (0.71 cm). Additionally, the fixed height F₁ may be a distance from 130 thousandths of an inch (0.33 cm) to 230 thousand of inches (0.58 cm) In a further embodiment, the fixed height F₁ may be 180 thousand of inches (0.46 cm). The heat H applied may be between 400° F. (204° C.) and 800° F. (426° C.) in one embodiment. In another embodiment, the heat H applied may be 600° F. (315.6° C.). The pressure P applied may be a continuous physical force to hold the unfused carpet layer 66 at the fixed height F₁. In one implementation the continuous physical force may squeeze the unfused carpet layer 66 at a fixed height.

At block 76, cooling C is applied to the unfused carpet layer 66 to form an initial fused carpet layer 78. By way of example and not by way of limitation, the cooling C operations may be executed by a cooling conveyor. In one embodiment, the cooling C applied may be a temperature at 35° F. (1.7° C.) to 100° F. (37° C.). In another embodiment, the cooling C applied may be 42° F. (5.6° C.). The cooling may be applied thermomechanically or by ambient conditions, for example.

At block 80, an iterative unfused carpet layer 82 is created by placing cleaned, unadulterated layers of carpet 84, 86 tufted side-to-tufted side with the initial fused carpet layer 78 interposed therebetween. The cleaned, unadulterated layer of carpet 86 includes a backing side 92 and a tuft side 94. The cleaned unadulterated layer of carpet 84 includes a backing side 88 and a tuft side 92. As previously mentioned, the cleaned, unadulterated layers of carpet 84, 86 may be sourced from various carpets, such as aforementioned polypropylene carpets, nylon 6 carpets, nylon 6,6 carpets, and polyester carpets, or combinations thereof, for example. The cleaned, unadulterated layers of carpet 84, 86 may be carpet waste that is sourced from landfill diversion or scraps and remainder pieces from new carpet production. The cleaned, unadulterated layers of carpet 84, 86 may be cleaned by a thorough combing and vacuuming to remove any debris. During the cleaning process, additional compounds and chemicals are not added, so that the carpet 84, 86 is unadulterated.

At block 96, heat H and pressure P are applied to the iterative unfused carpet layer 82 within the carrier 70 having the plates 72, 74 with a fixed height F₂. The fixed height F₂ may be greater than the fixed height F₁. In the illustrated embodiment, the carrier 70 in block 94 is identical to the carrier 70 in block 68. It should be appreciated that the carriers may be different in other implementations. By way of example and not by way of limitation, the heat H and pressure P operations may be executed by the heated conveyor as previously described.

In one embodiment, the fixed height F₂ may be a distance that is twice F₁. That is, the fixed height F₂ may be a distance from 160 thousandths of an inch (0.41 cm) to 560 thousand of inches (1.42 cm). Additionally, the fixed height F₂ may be a distance from 260 thousandths of an inch (0.66 cm) to 460 thousand of inches (1.17 cm). In a further embodiment, the fixed height F₂ may be 360 thousand of inches (0.91 cm). The heat H applied may be between 400° F. (204° C.) and 800° F. (426° C.) in one embodiment. In another embodiment, the heat H applied may be 600° F. (315° C.). The pressure P applied may be a continuous physical force to hold the iterative unfused carpet layer 82 at the fixed height F₂.

At block 98, cooling C is applied to the unfused carpet layer 82 to form an incremental fused carpet layer 100. By way of example and not by way of limitation, the cooling C operations may be executed by the cooling conveyor as previously described. In one embodiment, the cooling C applied may be a temperature at 35° F. (1.7° C.) to 100° F. (37° C.). In another embodiment, the cooling C applied may be 42° F. (5.6° C.)

At block 102, a further incremental unfused carpet layer is created by placing cleaned, unadulterated layers of carpet 104, 106 tufted side-to-tufted side with the incremental fused carpet layer 100 interposed therebetween. The cleaned, unadulterated layer of carpet 104 includes a backing side 108 and a tuft side 110. The cleaned, unadulterated layer of carpet 106 includes a backing side 112 and a tuft side 114. As previously mentioned, the cleaned, unadulterated layers of carpet 104, 106 may be sourced from various carpets, such as aforementioned polypropylene carpets, nylon 6 carpets, nylon 6,6 carpets, and polyester carpets, or combinations thereof, for example. The cleaned, unadulterated layers of carpet 104, 106 may be carpet waste that is sourced from landfill diversion or scraps and remainder pieces from new carpet production. The cleaned, unadulterated layers of carpet 104, 106 may be cleaned by a thorough combing and vacuuming to remove any debris. During the cleaning process, additional compounds and chemicals are not added, so that the carpet 104, 106 is unadulterated.

At block 116, heat H and pressure P are applied to the incremental unfused carpet layer 118 within the carrier 70 having the plates 72, 74 with a fixed height F_(n), which may be F₃, in instances where a third layer is being manufactured. In general, the fixed height F_(n) may be greater than the fixed height F₂ and the fixed height F₁. By way of example and not by way of limitation, the heat H and pressure P operations may be executed by the heated conveyor previously described at the heat H and pressure P conditions previously described. In one embodiment, the fixed height F_(n) may be n times F₁. So, when n equals 3, then the fixed height may be F_(n=3) may be 3 times F₁. Similarly, when n equals 4, then the fixed height may be F_(n=4) may be 4 times F₄.

At block 120, cooling C is applied to the incremental unfused carpet layer 118 to form a further incremental fused carpet layer 122. By way of example and not by way of limitation, the cooling C operations may be executed by the cooling conveyor previously discussed at the previously discussed cooling C.

At decision block 126, if the carpet waste composite 10 is complete, then the methodology ends at block 124. On the other hand, if additional incremental thickness is required, then the process returns to blocks 102, 116, and 120 to incrementally add another layer and F_(n) increases incrementally. As each layer is added, in one embodiment, the fixed height may incrementally increase by a fixed height equal to F₁. It should be appreciated that variations in the methodology of FIG. 2 are within the teachings presented herein. By way of example, the layers of carpet may be positioned tufted side-to-backing side or backing side-to-backing side at various stages in the methodology. That is, the layers of carpet may be positioned side-to-side, including tufted side-to-tuft side, tufted side-to-backing side, backing side-to-tufted side, or backing side-to-backing side. Further, at step 50, multiple layers of carpet, such as four, may be used initially or at other stages of the methodology to create the unfused carpet layer.

As mentioned, it should be appreciated that variations in the methodology of FIG. 2 are within the teachings presented herein. By way of further example, the unadulterated layers of carpet may include by weight percent, 1% to 5% of additives. By way of further example, the layers of carpet may include adhesive and binding contact therebetween provided by an adhesive or other binder of by weight percent, 1% to 5%.

Embodiments according to the teachings presented herein will now be illustrated by reference to the following non-limiting working examples wherein procedures and materials are solely representative of those which can be employed, and are not exhaustive of those available and operative. The following glossary enumerates the components utilized in the Examples and Test Methods presented hereinbelow.

Blended carpet is textile floor covering including nylon carpet and polyester carpet.

Nylon carpet is a textile floor covering including nylon 6 and nylon 6,6 yarns.

Polyester carpet is textile floor covering, including polyester yarns, normally composed of polyethylene terephthalate.

Example I. A carpet waste composite is made from a supply of cleaned, unadulterated layers of polyester carpet. The cleaned, unadulterated layers of polyester carpet were cleaned by a thorough combing and vacuuming to remove any debris. During the cleaning process, additional compounds and chemicals were not added, so that the polyester carpet is unadulterated. A composite construction material was formed with seventy-five (75) layers of the polyester carpet by initially placing two layers of the polyester carpet tufted side-to-tufted side with homogenous and non-adhesive, non-binding contact within the heated conveyor equipment with a fixed height of 70 thousand of inches (0.180 cm) at a heat of 540° F. (282.2° C.) and pressure of 1300 psi (about 8900 kPa) for 18 seconds. Cooling at 75° F. (23.9° C.) was then applied for 3 minutes. Iteratively, cleaned, unadulterated layers of carpet tufted side-tufted side were added with non-adhesive, non-binding contact under the same heat, pressure, and cooling process with an iterative height increase of 141 thousand of inches (0.360 cm).

Example II. A carpet waste composite is made from a supply of cleaned, unadulterated layers of blended carpet. The cleaned, unadulterated layers of blended carpet was cleaned by a thorough combing and vacuuming to remove any debris. During the cleaning process, additional compounds and chemicals were not added, so that the blended carpet is unadulterated. A composite construction material was formed with 35 layers of the blended carpet by initially placing two layers of the blended carpet tufted side-to-tufted side with homogenous and non-adhesive, non-binding contact within the heated conveyor equipment with a fixed height of 70 thousand of inches (0.180 cm) at a heat of 540° F. (282.2° C.) and pressure of 1300 psi (about 8900 kPa) for 18 seconds. Cooling at 75° F. (23.9° C.) was then applied for 3 minutes. Iteratively, cleaned, unadulterated layers of carpet tufted side-tufted side were added with non-adhesive, non-binding contact under the same heat, pressure, and cooling process with an iterative height increase of 141 thousand of inches (0.360 cm).

Example III. A carpet waste composite is made from a supply of cleaned, unadulterated layers of blended carpet. The cleaned, unadulterated layers of blended carpet was cleaned by a thorough combing and vacuuming to remove any debris. During the cleaning process, additional compounds and chemicals were not added, so that the blended carpet is unadulterated. A composite construction material was formed with 20 layers of the blended carpet by initially placing two layers of the blended carpet tufted side-to-tufted side with homogenous and non-adhesive, non-binding contact within the heated conveyor equipment with a fixed height of 70 thousand of inches (0.180 cm) at a heat of 540° F. (282.2° C.) and pressure of 1300 psi (about 8900 kPa) for 18 seconds. Cooling at 75° F. (23.9° C.) was then applied for 3 minutes. Iteratively, cleaned, unadulterated layers of carpet tufted side-tufted side were added with non-adhesive, non-binding contact under the same heat, pressure, and cooling process with an iterative height increase of 141 thousand of inches (0.360 cm).

Test Method I. Three carpet waste composites in accordance with teachings presented herein and manufactured in conformity with each of Example I, Example II, and Example III were tested according to the standard test method for plastic composite cross ties prescribed in the American Railway Engineering and Maintenance-of-way Association (AREMA) Guidance for Plastic Composite Cross Ties. This test method covers the determination of the properties of modules of elasticity, modulus of rupture, rail seat compression, single tie lateral push, spike/screw pullout, and thermal expansion. Table I, Table II, and Table III depict the AREMA Guidance for Plastic Composite Cross Ties test results for the Ex. I, Ex. II, and Ex. III Carpet Waste Composites.

TABLE I AREMA Guidance for Plastic Composite Cross Ties Test Results for Select Carpet Waste Composites in accordance with Example I AREMA Guidance for Plastic Composite Cross Ties (Example I) Modulus of Elasticity Min. - 170,000 psi PASSED Modulus of Rupture Min. - 2,000 psi PASSED Rail Seat Compression Min. - 900 psi PASSED Single Tie Lateral Push Min. - 2,000 lbf PASSED Spike/Screw Pullout Min. - 1,900/5,000 lbf PASSED Thermal Expansion Max. - 7.5 × 10⁻⁵ in/in/° F. PASSED

TABLE II AREMA Guidance for Plastic Composite Cross Ties Test Results for Select Carpet Waste Composites in accordance with Example II AREMA Guidance for Plastic Composite Cross Ties (Example II) Modulus of Elasticity Min. - 170,000 psi PASSED Modulus of Rupture Min. - 2,000 psi PASSED Rail Seat Compression Min. - 900 psi PASSED Single Tie Lateral Push Min. - 2,000 lbf PASSED Spike/Screw Pullout Min. - 1,900/5,000 lbf PASSED Thermal Expansion Max. - 7.5 × 10⁻⁵ in/in/° F. PASSED

TABLE III AREMA Guidance for Plastic Composite Cross Ties Test Results for Select Carpet Waste Composites in accordance with Example III AREMA Guidance for Plastic Composite Cross Ties (Example III) Modulus of Elasticity Min. - 170,000 psi PASSED Modulus of Rupture Min. - 2,000 psi PASSED Rail Seat Compression Min. - 900 psi PASSED Single Tie Lateral Push Min. - 2,000 lbf PASSED Spike/Screw Pullout Min. - 1,900/5,000 lbf PASSED Thermal Expansion Max. - 7.5 × 10⁻⁵ in/in/° F. PASSED

As shown by the results of Test Method I, the Ex. I, Ex. II, and Ex. III carpet waste composites exhibited passing performance under the American Railway Engineering and Maintenance-of-way Association (AREMA) Guidance for Plastic Composite Cross Ties, which examined modules of elasticity, modulus of rupture, rail seat compression, single tie lateral push, spike/screw pullout, and thermal expansion. Accordingly, the results of Testing Method I illustrates that the carpet waste composites manufactured in accordance with the teachings presented herein exhibit physical properties that are equivalent or better than those of existing plastic composite rail ties.

The order of execution or performance of the methods and steps illustrated and described herein is not essential, unless otherwise specified. That is, elements of the methods and steps may be performed in any order, unless otherwise specified, and that the methods may include more or less elements than those disclosed herein. For example, it is contemplated that executing or performing a particular element before, contemporaneously with, or after another element are all possible sequences of execution.

While this invention has been described with reference to illustrative embodiments, this description is not intended to be construed in a limiting sense. Various modifications and combinations of the illustrative embodiments as well as other embodiments of the invention, will be apparent to persons skilled in the art upon reference to the description. It is, therefore, intended that the appended claims encompass any such modifications or embodiments. 

1. A method of manufacturing a composite construction material, the method comprising: providing first, second, third, and fourth cleaned, unadulterated layers of intact carpet, each of the first, second, third, and fourth unadulterated layers of intact carpet having a backing side and a tufted side; creating an initial unfused carpet layer by placing the first and second cleaned, unadulterated layers of intact carpet tufted side-to-tufted side with homogenous and non-adhesive, non-binding contact therebetween; applying first heat and pressure to the unfused carpet layer within a first carrier having a first fixed height; applying first cooling to the unfused carpet layer to form an initial fused carpet layer; creating an iterative unfused carpet layer by placing the third and fourth cleaned, unadulterated layers of intact carpet tufted side-to-tufted side with the initial fused carpet layer interposed therebetween, the initial fused carpet layer forming non-adhesive, non-binding contact with each of the third and fourth cleaned, unadulterated layers of intact carpet; applying second heat and pressure to the iterative unfused carpet layer within a second carrier having a second fixed height, the second fixed height being greater than the first fixed height; and applying second cooling to the unfused carpet layer to form an iterative fused carpet layer.
 2. The method as recited in claim 1, wherein the first unadulterated layer of carpet further comprises nylon fibers.
 3. The method as recited in claim 1, wherein the first unadulterated layer of carpet further comprises polyester fibers.
 4. The method as recited in claim 1, wherein the first carrier further comprises first and second aluminum plates.
 5. The method as recited in claim 1, wherein the first fixed height further comprises a distance from 80 thousandths of an inch (0.20 cm) to 280 thousandths of an inch (0.71 cm).
 6. The method as recited in claim 1, wherein the first fixed height further comprises a distance from 130 thousandths of an inch (0.33 cm) to 230 thousandths of an inch (0.58 cm).
 7. The method as recited in claim 1, wherein the first fixed height further comprises a distance less than 200 thousandths of an inch (0.51 cm).
 8. The method as recited in claim 1, wherein the first fixed height further comprises a distance of 180 thousandths of an inch (0.46 cm).
 9. The method as recited in claim 1, wherein applying first heat and pressure further comprises applying heat between 400° F. (204° C.) and 800° F. (426° C.)
 10. The method as recited in claim 1, wherein applying first heat and pressure further comprises applying heat at 600° F. (315° C.)
 11. The method as recited in claim 1, wherein applying first heat and pressure further comprises applying a continuous physical force to hold the unfused carpet layer at the first fixed height.
 12. The method as recited in claim 1, wherein applying first cooling further comprises applying cooling at 35° F. (1.7° C.) to 100° F. (37° C.)
 13. The method as recited in claim 1, wherein applying first cooling further comprises applying cooling at 42° F. (5.6° C.)
 14. The method as recited in claim 1, wherein the second carrier and the first carrier are identical.
 15. The method as recited in claim 1, wherein the second carrier further comprises first and second aluminum plates.
 16. The method as recited in claim 1, wherein the second fixed height is twice the first fixed height.
 17. A method of manufacturing a composite construction material, the method comprising: providing first, second, third, and fourth cleaned, unadulterated layers of carpet, each of the first, second, third, and fourth unadulterated layers of carpet having a backing side and a tufted side; creating an initial unfused carpet layer by placing the first and second cleaned, unadulterated layers of carpet tufted side-to-tufted side with homogenous and non-adhesive, non-binding contact therebetween; applying first heat of at least 400° F. (204° C.) to the unfused carpet layer within a first carrier having a first fixed height, the first fixed height being a distance from 130 thousandths of an inch (0.33 cm) to 230 thousandths of an inch (0.58 cm); applying first cooling to the unfused carpet layer to form an initial fused carpet layer; creating an iterative unfused carpet layer by placing the third and fourth cleaned, unadulterated layers of carpet tufted side-to-tufted side with the initial fused carpet layer interposed therebetween, the initial fused carpet layer forming non-adhesive, non-binding contact with each of the third and fourth cleaned, unadulterated layers of carpet; applying second heat of at least 400° F. (204° C.) to the iterative unfused carpet layer within a second carrier having a second fixed height, the second fixed height being twice the first fixed height; and applying second cooling to the unfused carpet layer to form an iterative fused carpet layer.
 18. The method as recited in claim 17, wherein the first fixed height further comprises a distance of 180 thousandths of an inch (0.46 cm). 19.-20. (canceled) 